Features of titanium plate
- 1. The oxide film on the surface of the titanium seed plate is equivalent to a good durable wear-resistant hair separating agent. The use of the titanium seed plate saves the separating agent, makes the electrode plate easy to peel, and eliminates the pre-treatment process of the seed plate. The board is half lighter than the copper seed board.
- 2. The service life of the titanium seed plate is more than 3 times that of the copper seed plate, and can reach 10 to 20 years depending on the operating conditions
- 3. The electrolytic copper produced from the titanium seed plate has a dense crystal structure, a smooth surface and high quality.
- 4. Since the titanium seed plate does not need to be coated with a separating agent, the pollution of the copper electrolyte can be avoided.
- 5. Increase the production capacity and reduce the production cost of electrolytic copper, thereby having better economic benefits.
Titanium plate manufacturing process
- Hot forging is a forging process performed above the metal recrystallization temperature.
- Hot rolling is a rolling process performed at a temperature higher than the recrystallization temperature.
- Cold rolling A rolling process in which the plastic deformation temperature is lower than the recovery temperature.
- Annealing: A metal heat treatment process that slowly heats the metal to a certain temperature, keeps it for a sufficient time, and then cools it at an appropriate speed (usually slow cooling, sometimes controlled cooling).
- Pickling: The parts are immersed in an aqueous solution such as sulfuric acid to remove oxides and other films on the metal surface. It is the pretreatment or intermediate treatment of electroplating, enamel, rolling and other processes
Link to this article：Pure titanium plate and its titanium executive standard Titanium plate characteristics Titanium plate price
Reprint Statement: If there are no special instructions, all articles on this site are original. Please indicate the source for reprinting:Alloy Wiki，thanks！^^